Magerramov A. M., Ramazanov M. A., Gadjieva F. V.// The Journal of American Science. 2007. <...> Dudziak A., Jaskowska A., Borc R.// Current Topics in Biophysics. 2001. <...> Photoluminescent properties of nanocomposite materials on the base of PVDF+CdS and PP+CdS A. M. Magerramov, M. A. Ramazanov, F. V. Gadzhiyeva Baku State University, 23 Khalilov str., Baku, AZ1148, Azerbaijan E-mail: mamed_r50@mail.ru The photoluminescent properties of nanocomposite materials on the base of polyvinylidenefluoride (PVDF) with filler CdS were researched in the range = 300—1000 nm. <...> It is defined that polarity of polymer at other equal concentration essentially influences photoluminescent spectra nanocomposites. <...> It is experimentally established that in photoluminescent spectra basically varies the amplitude of a maximum connected with thickness and properties of a frontier layer and with recombination through levels of defects in a matrix and nanoparticles. <...> Изложены результаты исследования фотолюминесцентных свойств нанокомпозиций на основе поливинилиденфторида (ПВДФ) и полипропилена (ПП), обработанного под действием разрядной обработки в воздушной среде выше пробивной прочности воздуха и наполнителя CdS в интервале длин волн λ = 300—1000 нм. <...> Установлено, что в зависимости от времени разрядной обработки порошков полимера интенсивность фотолюминесценции увеличивается до 1 ч, а затем уменьшается. <...> Проведено сравнение спектров люминесценции нанокомпозиций на основе ПП+CdS и ПВДФ+CdS. <...> Экспериментально установлено, что в ФЛ-спектрах в основном меняется амплитуда максимума, связанная с толщиной и свойствами приграничного слоя и с рекомбинацией через уровни дефектов в матрице и наночастиц CdS! <...>