Chemistry 2 (2016 9) 243-251 ~ ~ ~ УДК 674.8 Increasing the Strength of Carbon Sorbents from the Extracted Larch Bark by Using Additives of Oil Bituminen Alexey V. Rudkovskiy, Olga Yu. <...> Fetisova and Nikolai V. Chesnokov* Institute of Chemistry and Chemical Technology SB RAS FRC “Krasnoyarsk Science Center SB RAS” 50/24 Akademgorodok, Krasnoyarsk, 660036, Russia Received 13.03.2016, received in revised form 29.04.2016, accepted 04.06.2016 The infl uence of oil bitumen additives to charcoals, obtained by the pyrolysis of the extracted larch bark on the properties of the active carbons was studied. <...> It was shown that the increase of the amount of bitumen in the charcoal reduces their sorption activity on iodine and rises their abrasion resistance. <...> It was found that after the impregnation of raw charcoal by 10 % solution of bitumen in toluene the sorption activity of activated carbon on iodine reaches 73 % and their abrasion resistance is more than 90 %. <...> All rights reserved * Corresponding author E-mail address: cnv@icct.ru # 243 # Alexey V. Rudkovskiy, Olga Yu. <...> Повышение прочности углеродных сорбентов из экстрагированной коры лиственницы путем использования добавок нефтебитума А.В. Рудковский, О.Ю. Фетисова, Н.В. Чесноков Институт химии и химической технологии СО РАН ФИЦ «Красноярский научный центр СО РАН» Россия, 660036, Красноярск, Академгородок, 50/24 Исследовано влияние нефтебитумных добавок к образцам угля-сырца, полученным пиролизом экстрагированной коры лиственницы, на свойства активированных углей. <...> Показано, что увеличение количества нефтебитума в углях-сырцах приводит к уменьшению их сорбционной активности по йоду и к увеличению прочности на истирание. <...> Установлено, что при пропитке исходного угля-сырца раствором 10%-го нефтебитума в толуоле активность по йоду активированного угля достигает 73 %, при этом прочность на истирание превышает 90 %. <...> В последнее время <...>